研究了不同等温退火工艺对8030铝合金导线组织及性能的影响。结果表明:等温退火前后合金均由α-Al基体和Al₆Fe相组成。在同一等温温度下,随着等温时间的延长组织逐渐趋于均匀化;同一等温时间下,随着等温温度的升高,组织趋于均匀化的时间缩短。经过等温退火处理后铝合金导线的导电率均有所提高,在470 ℃均匀化退火24 h后再经240 ℃等温4 h,合金导电率达到最高值57.21%IACS,比未经热处理试样的导电率提高了2.4%IACS。经过等温退火处理后铝合金导线的硬度及抗拉强度均有所降低,塑性大幅度提高。在470 ℃均匀化退火24 h后再经260 ℃等温8 h,合金的伸长率最高可达23.64%。热处理前后合金均为塑性断裂。     

强变形工艺对2519A铝合金组织与性能的影响

通过硬度测试、拉伸性能测试、透射电镜观察等分析手段研究了不同强变形工艺下2519A铝合金的力学性能与微观组织。结果表明,经50%的冷轧变形和165 ℃人工时效后,2519A合金的力学性能明显提高,其抗拉强度、屈服强度和伸长率分别为522 MPa、468 MPa和8.5%。而在冷变形前添加165 ℃×2 h预时效处理,合金的力学性能进一步提高,其抗拉强度、屈服强度和伸长率分别达到535 MPa、497 MPa和8%。预时效处理可以提高合金中θ′相的密度,使析出相分布更加均匀,有助于提高合金的力学性能。     

退火工艺对激光选区熔化成形Ti6Al4V合金组织及室温力学性能的影响

以Ti6Al4V球形粉末为原料,利用激光选区熔化成形方法制备了Ti6Al4V合金试样,采用光学显微镜、扫描电镜及力学性能测试等手段,研究了退火工艺对Ti6Al4V合金室温力学性能及组织的影响规律。结果表明: SLM成形沉积态Ti6Al4V合金室温抗拉强度超过1200 MPa,而平均断后伸长率仅为4.0%;在650 ℃下进行真空退火处理,合金的抗拉强度仍保持在1200 MPa左右,规定塑性延伸强度R_p0.2高于1150 MPa,但试样的断后伸长率<10%;而在750及800 ℃下进行真空退火处理,合金试样的抗拉强度降至1100 MPa左右,规定塑性延伸强度高于1050 MPa,伸长率达到甚至超过10%,材料的综合强韧性得到明显提升。随着真空退火加热温度和保温时间的增加,SLM成形Ti6Al4V合金原始β晶界逐渐变模糊,晶粒趋向于等轴化。与此同时,快速冷却转变的α′针状马氏体未出现明显地粗化。     

退火温度对HA/Ti-24Nb-4Zr复合材料组织与性能的影响

利用放电等离子烧结(SPS)技术制备了HA/Ti-24Nb-4Zr生物复合材料,研究了不同退火温度对复合材料显微组织和力学性能(抗压强度、屈服强度、屈强比、压缩弹性模量)的影响。结果表明,烧结态复合材料主要由β-Ti相、少量初生α-Ti相及HA相组成;随着退火温度的升高,复合材料基体中β-Ti相含量增多且晶粒逐渐长大,针状次生α-Ti相在晶界处和晶内不断析出,HA相结构和含量变化不大;与烧结态相比,不同退火温度处理后的复合材料强度和弹性模量先略微上升后下降,而塑韧性呈不断提高趋势;复合材料在850 ℃退火处理后,抗压强度、屈服强度、屈强比和压缩弹性模量值分别为1507 MPa、1270 MPa、0.84和42 GPa,塑韧性得到明显改善,作为生物医用植入材料具有潜在的应用前景。     

Feasibility of zeolites in converting butyric acid into propylene for biorefineries

The biorefinery has been recognized as a new industry to produce both energy and chemical materials such as olefins and BTX from renewable resources. In this context the conversion of butyric acid over zeolites was investigated for establishing a new production route of propylene. Propylene was mainly generated by decarbonylation and dehydration of butyric acid. Our study proved that H-ZSM-5 (750) and silicalite were the best industrial catalyst among the tested ones. For H-ZSM-5 (750), the selectivity of propylene reached 64.2 C% and the ratio of the yield for propylene to theoretical yield (75 C%) became 85.6%.     

Microwave-assisted metal-catalyzed pyrolysis of low-rank coal: Promising option towards obtaining high-quality products

Microwave-assisted catalytic pyrolysis is considered to be a promising technology for coal-staged conversion due to its high efficiency and selectivity. This work was undertaken to investigate the pyrolysis behavior and products quality of microwave-assisted pyrolysis of low rank coal catalyzed by metallic catalysts (K, Ca and Fe) with both dielectric response and catalytic effect via a microwave tube furnace. The mechanism of metallic catalysts on catalytic cracking tar under microwave radiation was also investigated. The dielectric properties and physicochemical structure of coal chars were characterized by a vector network analyzer, XRD, FT-IR, SEM, EDS, and Raman. The chemical structure characteristics of generated tars were determined by FT-IR and GC-MS. Results manifested that microwave interacted preferentially with metal catalysts by polarization and conductivity loss could efficiently induce the occurrence of catalytic pyrolysis reactions to generate high yield syngas (CO + H₂). Specifically, the dielectric loss factor of resultant chars was considerably improved with the introduction of metallic catalysts especial for Ca and Fe. Furthermore, it is found that metal catalysts dramatically enriched the amorphous carbon structure in produced chars whereas in favour of suppressing the trend of carbon graphitization. Additionally, the transformation of larger polycyclic aromatic compounds into lighter tar species was catalytically accelerated, resulting in the large proportion of single-ring aromatics in tar under the synergistic effect between microwave and metal catalysts.     

Effects of water-soluble soybean polysaccharide on rheological properties,stability and lipid digestibility of oil-in-water emulsion during in vitro gastrointestinal digestion

Water-soluble soybean polysaccharide (SSPS) is a naturally occurring emulsifier. SSPS was used as the sole emulsifier to stabilize an oil-in-water (O/W) emulsion. The effects were investigated of different SSPS concentrations (3–20% (w/w)) on the lipid digestibility, rheological properties and stability of O/W emulsions during in vitro digestion model. The droplet size of the emulsions tended to increase during the oral phase because the emulsions were unstable and droplets coalesced, except with a SSPS concentration of 20% (w/w). The presence of SSPS markedly reduced the free fatty acid (FFA) content after its stabilized O/W emulsion passed through in vitro gastrointestinal digestion. The amount of FFA significantly decreased as the concentration of SSPS increased due to SSPS stabilization film on oil droplet surface and high viscous system. SSPS may be an attractive alternative ingredient to control the lipid digestibility of emulsions for various food products.     

页岩气地质评价关键实验技术的进展与展望

页岩气地质评价实验结果为页岩气地质"甜点"评价、地质选区、储量计算、水平井压裂层段优选及开发方案确定等提供了重要的数据基础与科学依据。近年来,随着我国页岩气勘探开发工作的不断深入,相关地质评价实验技术也取得了较大的进展。特别是在页岩微观孔隙结构、含气性和物性这3个方面,通过引进先进技术与自主设备研发相结合,建立了适用于我国海相页岩的分析测试技术和标准,对于推动我国页岩气的勘探开发进程发挥了重要的作用。为了给我国页岩气基础地质研究、实验室建设及相关标准制定提供参考和指导,归纳总结了国内外在上述3项页岩气地质评价关键实验技术方面所取得的进展,并对相关技术未来的发展趋势进行了展望。研究结果表明:①对于页岩微观孔隙结构测试,目前已经形成了多种手段相结合的定性观测和定量表征测试方法,实现了由静态表征向动态表征的转化,未来需要在页岩孔隙结构的原位表征和孔内流体赋存特征直接观测等方面做进一步的研究;②对于页岩含气性测试,目前已经建立了现场与室内相结合的含气性定量表征系列技术,实现了对页岩吸附气和游离气赋存特征的定量评价,未来需要在深层页岩损失气量计算、页岩气吸附机理及模型等方面做进一步的研究;③对于页岩物性测试,目前已经建立了多种方法相结合的孔隙度和渗透率测试技术,实现了对页岩孔隙有效性的定量评价,未来需要在孔隙度测试条件和方法等方面进行对比研究并统一标准。结论认为,只有不断地改进和优化页岩气地质评价实验技术,才能够满足科研与生产的需求。     

混炼方式对螺旋纳米碳纤维增强天然橡胶复合材料力学性能的影响

采用干法和湿法两种混炼工艺制备了螺旋纳米碳纤维(HCNFs)/炭黑(CB)/天然橡胶(NR)复合材料,通过扫描电镜、拉伸试验机和应变扫描仪分别对所制备复合材料的界面形貌、力学性能和Payne效应进行了测试分析,考察了混炼方式对复合材料宏观力学性能及Payne效应的影响。结果表明,与纯CB填料相比,在干湿两种混炼方式下,添加适量的HCNFs(1～6份)能提高HCNFs/CB/NR复合材料的300%定伸应力、扯断伸长率、拉伸强度和硬度。与干法混炼相比,湿法混炼能明显增强HCNFs/CB/NR复合材料的Payne效应,并提升在HCNFs高添加量(2～6份)条件下的拉伸强度和扯断伸长率,这主要源于湿法混炼能够有效改善HCNFs在橡胶基质中的分散性。